性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 527600（8,320)kg/cm²(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527 %拉伸模量 ASTM D638/ISO 527 kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 527100%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527 %弯曲模量(弯曲弹性率) ASTM D790/ISO 17825100(35000)kg/cm²(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 178910(12,900)kg/cm²(MPa)[Lb/in2]洛氏硬度 ASTM D785 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 17965kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.18 成型收缩率 ASTM D9550.4-0.6%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133 g/10min220℃/10kgASTM D1238/ISO 1133 g/10min吸水率 23℃/24H ASTM D570/ISO 620.4%热性能热变形温度退火ASTM D648/ISO 75 ℃（℉）未退火ASTM D648/ISO 7592(197)℃（℉）维卡软化点 ASTM D1525/ISO R306107(225)℃（℉）熔点 - ℃（℉）燃烧性（率） UL941.5mmV-0 2.0mm5VB 线性膨胀系数 ASTM D696/ISO 1135922mm/mm.℃电气性能介电常数100HZASTM D150/IEC 60250 1MHZASTM D150/IEC 60250 体积电阻率 ASTM D257/IEC 60093 Ω.cm表面电阻率 ASTM D257/IEC 60093 Ω耐电弧性 ASTM D495/IEC 60112 加工条件干燥条件 加工温度射嘴 ℃料筒前段 ℃料筒中段 ℃料筒后段 ℃熔体温度 ℃模具温度 ℃压力注塑压力 Mpa保压压力 Mpa背压 Mpa螺杆转速 rpm其他备注 颜色 特性OA部品用途 "};